超声波清洗机使用产生空化效应的超声波在液体,可以去除石油从工件表面,配合适当的清洁剂,工件表面可以迅速达到高清洁度。电镀过程中,工件表面清洁度要求高,超声波清洗是可以满足要求的。

Ultrasonic cleaning machine can remove oil from the surface of the workpiece by using the ultrasonic wave which produces cavitation effect in the liquid. With the appropriate cleaning agent, the surface of the workpiece can quickly achieve high cleanliness. In the electroplating process, the workpiece surface cleanliness requirements are high, ultrasonic cleaning can meet the requirements.

超声波清洗机的使用,可以替代溶剂清洗油;可以取代电解除油;可以取代酸蚀刻去除表面的锈蚀碳钢和低合金钢和规模。超声波清洗机的应用,可以使许多传统清洗过程简化,大大提高清洗质量和生产效率。特别是对于形状更复杂和要求较高的工件边缘有更多的优点。使用超声波清洗机技术在广泛的替代角色的强酸、强碱、大大减少和环境污染,改善劳动环境,减轻劳动强度,保护生态环境,做出贡献。

The use of ultrasonic cleaning machine can replace solvent cleaning oil; it can replace electrolytic degreasing; it can replace acid etching to remove rust carbon steel and low alloy steel on the surface. The application of ultrasonic cleaning machine can simplify many traditional cleaning processes and greatly improve the cleaning quality and production efficiency. Especially for the workpiece edge with more complex shape and higher requirements, it has more advantages. The use of ultrasonic cleaning machine technology in a wide range of alternative role of strong acid, strong alkali, greatly reduce and environmental pollution, improve the labor environment, reduce labor intensity, protect the ecological environment, make contributions.

1、抛光膏抛光表面的清洁。

1. Cleaning of polished surface with polishing paste.

在正常情况下,抛光膏经常使用石蜡混合、石蜡分子重量,高熔点,正常温度是固体,更难以清洁的材料,传统的方法是使用有机溶剂清洗或高温碱煮,有许多弊病。使用超声波清洗可以使用水基清洗剂,的情况下,介质温度,在几分钟内将彻底地清洗表面,常用的过程是:

Under normal conditions, polishing paste often uses paraffin mixture, paraffin molecular weight, high melting point, normal temperature is solid, more difficult to clean materials, the traditional method is to use organic solvent cleaning or high temperature alkali boiling, there are many disadvantages. When ultrasonic cleaning is used, water-based cleaning agent can be used. In case of medium temperature, the surface will be thoroughly cleaned in a few minutes. The common process is as follows:

(1)浸泡,(2)超声波清洗——(水)(3)水冲洗。

(1) Soaking, (2) ultrasonic cleaning - (water) (3) water washing.

2、表面的油和少量的生锈的冷轧钢板。

2. Oil on the surface and a small amount of rusty cold rolled steel plate.

一般有冷轧钢板表面油污、灰尘或少量的铁锈,洗干净容易,但是在一般的方法来清洁表面仍然是一个非常薄的一层浮灰,影响后续加工质量,有时可能不再使用酸浸法去除这一层浮灰。和使用适当的超声波清洗和清洁液,可以方便地实现彻底清洁表面,使工件表面具有高的活动,有时甚至撤销酸洗电镀前激活过程。

Generally, there are oil, dust or a small amount of rust on the surface of cold-rolled steel plate, which is easy to clean. However, the surface is still a very thin layer of floating ash in the general method, which affects the quality of subsequent processing. Sometimes, acid leaching method may not be used to remove this layer of floating ash. It is easy to clean the surface thoroughly by using appropriate ultrasonic cleaning and cleaning solution, which makes the surface of workpiece have high activity, and sometimes even cancel the activation process before pickling and electroplating.

3、表面的氧化皮和条锈病的工件。

3. The surface of the oxide skin and rust on the workpiece.

传统的方法是用盐酸或硫酸浸泡清洗。如使用超声综合处理技术,可以快速在几分钟,去除油、锈表面的工件,避免由于强酸清洗与氢脆。

The traditional method is to soak and clean with hydrochloric acid or sulfuric acid. If the ultrasonic comprehensive treatment technology is used, the workpiece on the oil and rust surface can be removed quickly in a few minutes to avoid strong acid cleaning and hydrogen embrittlement.